Irradiation-Assisted Stress Corrosion Cracking Susceptibility and Evolution of Microstructure in Several Nickel-Base Alloys after Proton Irradiation
For long-term operations of existing nuclear plants and the design of next-generation plants, it is desirable to develop more radiation-resistant materials for reactor core components. This report describes the impacts of proton irradiation on four nickel-base alloys, with a focus on microstructure, irradiation hardening, and susceptibility to stress corrosion cracking. It was prepared as part […]